PEI/APP改性脲醛树脂制备阻燃胶合板及性能

以聚乙烯亚胺(PEI)为改性剂处理聚磷酸铵(APP)制备得到APP@PEI阻燃体系,并将其加入到脲醛树脂(UF)中,制备阻燃胶合板。研究了APP@PEI对UF胶黏剂理化性能的影响,并进一步探讨其对胶合性能及阻燃性能的影响。结果表明:APP、PEI和APP@PEI对UF的黏度、pH和固化时间均有影响。当APP添加量为10%时,UF的黏度由3.843 Pa·s上升至8.270 Pa·s,pH降至5.67,固化时间由91 s降至87 s;当PEI添加量为0.91%时,由于UF体系中支化和交联程度增加,黏度上升至41.433 Pa·s,pH和固化时间分别提升至9.91和116.3 s;而APP@PEI能降低对UF各项性能的影响,添加10%APP@PEI时UF的黏度、pH和固化时间分别为5.966 Pa·s、6.33和94.3 s。添加APP后,胶合板的胶合强度均低于Ⅱ类胶合板强度标准(0.7 MPa);添加PEI后,胶合板的胶合强度能够提升18%以上;APP@PEI添加量为10%时,胶合板的胶合强度达0.85 MPa,高于Ⅱ类胶合板强度标准要求。添加APP、PEI和APP@PEI对胶合板的阻燃性能有不同影响,单独添加PEI无法改善胶合板的阻燃性能,当APP和APP@PEI添加量为10%,15%和20%时,胶合板的极限氧指数(LOI)分别比未添加阻燃剂时提高0.8%,2.0%,2.5%和1.2%,2.2%,3.1%。     

沙柳液化产物/异氰酸酯泡沫材料热学性能研究

为探究阻燃剂对沙柳液化产物/异氰酸酯泡沫材料导热行为的影响和开发具有阻燃特性的聚合物复合材料，以沙柳多元醇液化产物为原料、辛酸亚锡为催化剂、水为发泡剂，与异氰酸酯进行发泡制备沙柳液化产物/异氰酸酯硬质泡沫，利用正交试验法研究工艺因子对硬质泡沫材料导热性能的影响规律，使用锥形量热仪（CONE）对该材料燃烧行为进行分析。结果表明:1）沙柳液化产物/异氰酸酯泡沫材料制备工艺对导热性能的影响关系为阻燃剂添加量＞沙柳液化产物与异氰酸酯比例＞阻燃剂种类，方差分析表明工艺因子对导热性能的影响均不显著；2）最优工艺:阻燃剂添加量8%，沙柳液化产物/异氰酸酯比例1.0∶1.0，阻燃剂为有机蒙脱土，制备的硬质泡沫材料密度0.168 g·cm^-3，抗压强度0.83 MPa，导热系数0.118 3 W·m^-1·K^-1，此工艺制备的聚氨酯泡沫是一种优良的保温材料；3）不同有机蒙脱土添加量的沙柳液化产物/异氰酸酯泡沫燃烧行为属于双阶段燃烧过程，阻燃剂有机蒙脱土添加量8%，燃烧开始时间推迟至120 s且总热释放量降低。     

BL-环保阻燃剂在单板上载药量影响因素的初步研究

单板中阻燃剂载药量的多少直接影响着阻燃胶合板的阻燃性能。单板进行阻燃剂浸泡过程中,影响其载药量的因素较多,如单板初含水率、浸泡时间、阻燃剂浓度及阻燃剂温度等。对影响单板载药量的因素做了初步试验研究并对试验结果进行了分析,同时结合国内实际生产情况给出了建议。     

环保阻燃胶的开发

为了改善人造板的阻燃性能及降低人造板游离甲醛释放量，在引进国外先进技术基础上，历经两年的消化、吸收、创新工作，开发出一种集环保、阻燃、抑烟、胶粘于一体的环保型阻燃胶。实验室及福州人造板厂生产性试验结果表明，这种胶粘剂符合中密度纤维板生产的要求，可生产出低游离甲醛释放的阻燃中密度纤维板。初步的成本分析表明，与常用阻燃剂相比，这种阻燃胶在价格上极具优势。     

Use of the BCR three-step sequential extraction procedure for the study of the partitioning of Cd, Pb and Zn in various soil samples

A slightly modified three-step sequential extraction procedure proposed by the Community Bureau of Reference (BCR) for analysis of sediments was successfully applied to soil samples. Contaminated soil samples from the lead and zinc mining area in the Mezica valley (Slovenia) and natural soils from a non-industrial area were analysed. The total concentrations of Cd, Pb and Zn and their concentrations in fractions after extraction were determined by flame or electrothermal atomic absorption spectrometry (FAAS, ETAAS). Total metal concentrations in natural soils ranged from 0.3 to 2.6 mg kg^-1 for Cd, from 20 to 45 mg kg^-1 for Pb and from 70 to 140 mg kg^-1 for Zn, while these concentrations ranged from 0.5 to 35 mg kg^-1 for Cd, from 200 to 10000 mg kg^-1 for Pb and from 140 to 1500 mg kg^-1 for Zn in soils from contaminated areas. The results of the partitioning study applying the slightly modified BCR three-step extraction procedure indicate that Cd, Pb and Zn in natural soils prevails mostly in sparingly soluble fractions. Cd in natural soils is bound mainly to Fe and Mn oxides and hydroxides, Pb to organic matter, sulphides and silicates, while Zn is predominantly bound to silicates. In contaminated soils, Cd, Pb and Zn are distributed between the easily and sparingly soluble fractions. Due to the high total Cd, Pb and Zn concentrations in contaminated soil close to the smelter, ! and their high proportions in the easily soluble fraction (80% of Cd, 50% of Pb and 70% of Zn), the soil around smelters represents an environmental hazard.     

微波消解-FAAS测定番木瓜不同部位的金属元素含量

为探讨番木瓜果肉、果皮、瓜籽中金属元素的含量,采用微波消解-FAAS法测定了番木瓜3个部位的K、Na、Ca、Mg、Cu、Fe、Zn共7种金属元素的含量,并对微波消解条件进行了优化。结果显示,在优化的微波消解条件下,样品消解完全、速度快、效果好,FAAS测定的各金属元素质量浓度与吸光度均呈良好的线性关系,相关系数r为0.995 7～0.999 9,检出限为0.002～0.131,回收率为98.30%～101.67%,RSD为0.20%～4.12%(n=6),说明测定方法可靠,结果稳定;番木瓜3个部位均含有较高的K、Ca、Mg,但Cu、Fe、Zn含量均较低,与番木瓜果肉相比,番木瓜果皮和瓜籽中K、Mg、Cu、Zn、Fe含量较高,食品和药品开发优势更突出。     

微波消解-FAAS测定虾肉中钙的质量分数

采用微波消解-火焰原子吸收光谱法（flame atomic absorption spectrometry，FAAS）测定虾肉中钙（ca）元素的质量分数，对微波消解前处理的条件进行了研究。试验结果显示，最佳的微波消解体系为取样量0．500g，以硝酸（HNO，）作为消解溶剂，用量5．0mL，最适微波消解程序为多步消解程序D，包含3个步骤：1）功率400W，比例100％，升温5min，消解温度120℃，保持5min；2）功率800W，比例100％，升温5min，消解温度150℃，保持10min；3）功率800W，比例100％，升温10min，消解温度180℃，保持10min。样品消解液在常温或冷藏条件下保存48h之内的稳定性良好。经微波消解前处理后虾肉样品中”（ca）的相对标准偏差（relative standard deviation，RSD）为5．284％，加标回收率为91％-98％。微波消解-FAAS测定虾肉中的w（Ca）具有样品处理时间短、试剂用量少、结果准确和安全性高等优点。     

阻燃处理竹篾层积材的性能分析

采用M1和M2两种阻燃剂,通过冷热槽法,浸渍处理竹篾后制备竹篾层积材,测定其氧指数、热释放速率、发烟总量等燃烧性能,以及静曲强度、弹性模量等物理力学性能.结果表明:经2种阻燃剂处理,竹篾层积材的耐火性能大幅提高,尤其是M2处理的层积材,综合燃烧性能好;虽板材的力学性能都有一定程度的下降,但仍能满足LY/T 1072-2002的要求.     

森林火灾图像几何特征提取识别的算法研究

根据野外森林环境下早期烟火的火焰特征,描述了火焰识别的-般判断方法,本研究在原判断基础上利用火焰几何特征来提高火焰判断精度的方法,提出了圆形度、矩形度、平均密度和偏心度4种算法作为火焰儿何特征的判断依据.与其它的火焰识别方法相比较,该算法在野外的复杂环境中,识别的准确性更高,抗干扰能力更强.     

浊点萃取—火焰原子吸收光谱法测定水样中的痕量锌

研究了以1-(2-吡啶偶氮)-2-萘酚为配位剂,Triton X-114为非离子表面活性剂,硝酸-甲醇为黏度调节剂,浊点萃取-火焰原子吸收光谱法测定锌的方法,对试验条件进行了优化。在最佳条件下,锌的检测限为0.687μg/L,富集倍数为66。对水样中锌的含量进行了测定,加标回收率为95%~102%。